In this paper, the effect of polypropylene fibers (PF) on fresh and hardened properties of cement mortars
produced with white cement is reported. Nine mixtures were prepared by using different volume fractions and
different sizes of PF from 0 to 1.5% and 6 and 12 mm, respectively. Water to cement and sand to cement ratio
by weight was kept constant as 0.4 and 3.0, respectively. PF with different length and amounts was introduced
to mixtures and its effect on workability, density, water absorption, compressive strength, flexural strength
and drying shrinkage were determined. Pore ratio at the cross-section of the specimens was calculated by
image analysis. Test results showed that the addition of PF in higher amounts decreased workability, fresh and
hardened density, compressive and flexural strength and increased water absorption and pore ratio of the
mixtures. However when used in lower amounts, PF improved drying shrinkage and flexural strength.

Bu çalışmada, polipropilen lifin (PF) beyaz çimento harcı ile üretilmiş çimento harcının taze ve sertleşmiş
özelliklerine etkisi incelenmiştir. Farklı oranlarda (hacimce %0-%1,5) ve farklı uzunluklarda (6 ve 12mm)
polipropilen lifler kullanılarak, toplam 9 seri üretilmiştir. Su/çimento oranı ve kum/çimento oranı, sırası ile 0,4
ve 3 olmak üzere sabit tutulmuştur. Farklı uzunluk ve miktardaki polipropilen lifler karışıma katılmış ve
liflerin harcın, işlenebilirlik, yoğunluk, su emme, basınç dayanımı, eğilme dayanımı ve kuruma rötresine olan
etkileri araştırılmıştır. Boşluk oranı, numune en kesitinden Image Analiz (Image Analysis) yöntemi ile
belirlenmiştir. Deney sonuçlarına göre yüksek miktarda PP lif kullanımı, işlenebilirliğin, taze ve sertleşmiş
yoğunluğun, basınç ve eğilme dayanımının azalmasına ve boşluk oranı ve su emme miktarının artmasına
neden olmuştur. Düşük oranda PP kullanımı, kuruma rötresi ve eğilme dayanımını iyileştirmiştir